• Steel Lined Plastic LLDPE Spray Tower Tank for Chemical Corrosion Resistant (Desulfurization, Acid washing, Wast Gas Treatment)
  • Steel Lined Plastic LLDPE Spray Tower Tank for Chemical Corrosion Resistant (Desulfurization, Acid washing, Wast Gas Treatment)
  • Steel Lined Plastic LLDPE Spray Tower Tank for Chemical Corrosion Resistant (Desulfurization, Acid washing, Wast Gas Treatment)
  • Steel Lined Plastic LLDPE Spray Tower Tank for Chemical Corrosion Resistant (Desulfurization, Acid washing, Wast Gas Treatment)
  • Steel Lined Plastic LLDPE Spray Tower Tank for Chemical Corrosion Resistant (Desulfurization, Acid washing, Wast Gas Treatment)
  • Steel Lined Plastic LLDPE Spray Tower Tank for Chemical Corrosion Resistant (Desulfurization, Acid washing, Wast Gas Treatment)

Steel Lined Plastic LLDPE Spray Tower Tank for Chemical Corrosion Resistant (Desulfurization, Acid washing, Wast Gas Treatment)

After-sales Service: 24
Warranty: 24
Condition: New
Customized: Customized
Tank Marerial: Metal Tank
Type: Horizontal / Vertical
Customization:

Contact Supplier

Diamond Member Since 2015

Suppliers with verified business licenses

5.0
Audited Supplier

Suppliers reviewed by inspection services.

Manufacturer/Factory, Trading Company, Group Corporation
  • Overview
  • Certifications
  • Packaging & Shipping
  • FAQ
Overview

Basic Info.

Model NO.
Acid Washing tower tank
Storage Objects
Liquid
Materical
Q235A + PE (Plastic )16mm -22mm
Type H
Horizontal / Vertical
Transport Package
Nil
Specification
OEM
Trademark
Dong Run Ze
Origin
China
HS Code
73090000
Production Capacity
8000

Product Description

 Tank LLDPE Lined Can Customizing For  Steel Lined Plastic LLDPE Spray Tower Tank For Chemical Corrosion Resistant (Desulfurization ,Acid washing, Wast Gas Treatment )


Electrolytic polishing equipment  Acid Tank For Metal Dipping

Electrolytic Polishing Tank / Can /Pool Pipe Unit, Electrolytic Cleaning Tank,Acid Polishing Tank
Steel Lined Plastic LLDPE Spray Tower Tank for Chemical Corrosion Resistant (Desulfurization, Acid washing, Wast Gas Treatment)Steel Lined Plastic LLDPE Spray Tower Tank for Chemical Corrosion Resistant (Desulfurization, Acid washing, Wast Gas Treatment)Steel Lined Plastic LLDPE Spray Tower Tank for Chemical Corrosion Resistant (Desulfurization, Acid washing, Wast Gas Treatment)


Metal cans Steel-Lined Plastic Square Tank, Electrolytic Tank, Pickling Tank  Acid Containment Vessels Custom Made Rotationally Molded Linear Resins LLDPE
Custermizing Checmial Acid Storage Tank 60 m3 Steel Lined LLDPE  Tank Used to Contain: HCl (max 35%) , Naoh (max 50%) , Naclo (max 10%) , PAC (max 17%) ,H2so4  

Used to contain: HCl (max 35%), NaOH (max 50%), NaCLO (max 10%), PAC (max 17%), H2SO4 etc 


 Media (density) : (1155 Kg/m3), Hydrochloric Acid (1150 Kg/m3), Sulfate, Nitrate (1152 Kg/m3), Phosphate (1151 Kg/m3), Hydrofluoric Acid (1132 Kg/m3), Battery Fluid (1135 Kg/m3), Chloride (1135 Kg/m3), Ferric Chloride Solution (1130 Kg/m3), Sodium Hypochlorite (1130 Kg/m3), Sulfurous Acid (1030 Kg/m3)

processing/storing; aluminum sulfate, ammonium sulfate, calcium chloride, ethylene glycol, ferric chloride, ferric sulfate, ferrous sulfate, hydrochloric acid, hydrofluoric acid, hydrofluosilicic acid, hydrogen peroxide, magnesium chloride, phosphoric acid, polymers, potassium hydroxide, or just plain water and we'll design the vessel(s) you require.

Horizontal / Vertical Storage HCL Acid Tanks Steel Lined LDPE 120000 Liters 
For Storage Bleach, Hydrochloric Acid, Ferric Chloride, Oilfield Chemicals, Corrosive Wastes And Other Hazardous Cargoes. 
Steel ( 6 mm -8mm ) Lined PE Plastic 7042 (16mm - 25 mm ) storage tank

Detail Picture

Steel Lined Plastic LLDPE Spray Tower Tank for Chemical Corrosion Resistant (Desulfurization, Acid washing, Wast Gas Treatment)

Steel Lined Plastic LLDPE Spray Tower Tank for Chemical Corrosion Resistant (Desulfurization, Acid washing, Wast Gas Treatment)
Steel Lined Plastic LLDPE Spray Tower Tank for Chemical Corrosion Resistant (Desulfurization, Acid washing, Wast Gas Treatment)
Steel Lined Plastic LLDPE Spray Tower Tank for Chemical Corrosion Resistant (Desulfurization, Acid washing, Wast Gas Treatment)
Steel Lined Plastic LLDPE Spray Tower Tank for Chemical Corrosion Resistant (Desulfurization, Acid washing, Wast Gas Treatment)


 
Steel Lined Plastic LLDPE Spray Tower Tank for Chemical Corrosion Resistant (Desulfurization, Acid washing, Wast Gas Treatment)
 
 
Certifications

Steel Lined Plastic LLDPE Spray Tower Tank for Chemical Corrosion Resistant (Desulfurization, Acid washing, Wast Gas Treatment)

Packaging & Shipping

Steel Lined Plastic LLDPE Spray Tower Tank for Chemical Corrosion Resistant (Desulfurization, Acid washing, Wast Gas Treatment)
 

FAQ

 1.Are you trading company or manufacturer ? 

         We are Group Corporation manufacturer ,have Group Factories Contractor.

  2 .Can I have samples of this type of product to test the quality?
      Yes, you can buy any sample to test the quality,our MOQ is 1 unit.

  3. What's the delivery time and can you lower the price? 
    It depends on your order.The delivery time is within 30 workdays after we received your prepayment. If you have placed an order of large quantities, then,of course, the price can be lowered.
 
4.Can you supply some quick-wear parts? 
Yes, we can supply the parts as your request,such as traction,traction pin,balance beam and plate spring,hanging accessories,turntable,all kinds of brake pads,brake pan, bearings,etc.
 
6.Do you have any used products for sale? 
We have products in stock for choices,the prices are favorable,we'll show you our stock products if you need.

7.What's the payment terms?
 TT 30% as deposit, balance before shipment by TT or at sight.

8. How to guarantee customers get the goods smoothly after they payment? 
Don't worry,dear.We have joined the trade assurance,you can place the order by trade assurance,if we don't delivery products, the deposit will be returned to you.

9.How can you ensure the quality of the products? 

Don't worry,dear.We have joined the trade assurance,if the products have quality problems when you received them,the payments can be refund to you.


There are five commonly used wrecker tow truck , usually depending on the type or size of the recovery wrecker :
First type : Boom towing truck

- use adjustable arms and winches to retract vehicles from ditches, embankments, or any vehicle that cannot arrive safely. Some booms are fixed, some heavy rotating racks, hydraulic telescopic tubes, others. In the past boom, trucks used the "hook chain" system, the chain around the frame or axle, and then hoisted by the winch. A heavy rubber pad is attached to the truck and truck so that it can be towed onto other bridges." Slings and belts are an evolution, replacing parts of chains with rubber belts.  slings did not use too much today because they could shave bumper cars. But they are sometimes used in wrecker accidents carrier or have one or two front wheels or rear wheels missing or pickups and other vehicles have steel bumpers. Equipped with all wheel drive, the truck is towed away, unable to use the machine string, because it can make the car power transmission system problems.

Second type :Wheel lift wrecker towing truck  

(also called "glasses") - from the chain hook technique to generate a large metal frame, can be installed in the front or rear under the cradle, rendering vehicles by pneumatic or hydraulic hoist can drag the ground clear front or rear. The device usually picks up the wheel of the vehicle (i.e., front wheel, if it is front wheel drive, rear wheel, if it is rear wheel drive), and contacts the tire.   wheel lift wrecker tow truck are common in china; cradles are like glasses. Medium and heavy-duty trucks use variations, "underlift" or "chassis lift", in which the elevator shaft or frame is not the wheel. A forklift truck can be used as an adapter or a lift chassis.

Third type :Integration towing truck  (also known as "Self Loader wrecker equipment", "Snatcher towing vehicle", "quick choice tow truck" or "roll back wrecker") - the arm and wheel lift together. Used of light trucks to recover or stop vehicles. Most of the truck's cab equipment is controlled so that the pickup truck does not leave the truck to connect the vehicle.  heavy trucks are also manufactured using integrated lifts.

Forth type --Flat plates wrecker truck  (also known as "rolling back tow truck" or "sliding tow truck") - the entire back of the truck is fitted with a bed that can be hydraulically tilted down to the ground, allowing the vehicle to be placed under its own power or pulled up by the winch. [9] because they carry, rather than traction vehicles, it can be completely fixed; in the United States, they carry serious damage to car accidents.

Fifth type ---Lifting platform  wrecker truck the derricks lift the vehicle vertically and use the wheel lift to load it on the bed. In Europe, this car can eliminate the parallel parking of vehicles.



Steel Lined Plastic LLDPE Spray Tower Tank for Chemical Corrosion Resistant (Desulfurization, Acid washing, Wast Gas Treatment)

 

 


Rotationally Molded LLDPE TANK
 chemical resistance of LLDPE   
 Cell / :+8615271357675   
 tictrucks.en.made-in-china.com   

LDPE / HDPE Chemical Resistance Chart 

The chemical compatibility of LDPE and HDPE on this chart is tested at 20°C: and 50°C: for 7 days and 30 days (if applicable) with constant exposure.

LDPE & HDPE resistance listed by chemical
1.4-dioxaneLDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE at 50°C: shows some effect after 7 days.
AcetaldehydeLDPE / HDPE at 20°C: little or no damage after 30 days.
HDPE at 50°C: shows some effect after 7 days.
LDPE at 50°C: immediate damage may occur.
Acetic Acid 5 %LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Acetic Acid, glacial 50%LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE at 50 °C: immediate damage may occur.
AcetoneLDPE / HDPE at 20°C-50°C: damage may occur.
Not recommended for continuous use.
Allyl AlcoholLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Aluminum saltsLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Amino acidsLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
AmmoniaLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ammonium carbonate saturatedLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ammonium phosphateLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ammonium sulphateLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Amyl chlorideHDPE at 20°C: shows some effect after 7 days.
HDPE at 50°C & LDPE at 20°C-50°C: immediate damage may occur.
Not recommended for continuous use.
AnilineLDPE / HDPE at 20°C: little or no damage after 30 days.
HDPE at 50°C: shows some effect after 7 days.
BenzeneLDPE / HDPE at 20°C-50°C: damage may occur.
Not recommended for continuous use.
Benzyl alcoholLDPE / HDPE at 50°C: immediate damage may occur.
HDPE at 20°C: shows some effect after 7 days.
Boric acidLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
BromineLDPE / HDPE at 50°C: immediate damage may occur.
HDPE at 20°C: shows some effect after 7 days.
Butyric acidLDPE / HDPE at 50°C: immediate damage may occur.
HDPE at 20°C: shows some effect after 7 days.
Calcium chlorideLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Calcium hydroxide saturatedLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Carbon tetrachlorideHDPE at 20°C: shows little or no damage after 30 days.
LDPE at 20°C & HDPE at 50°C: show some effect after 7 days.
LDPE at 50°C: not recommended.
Chlorine 10% in waterLDPE / HDPE at 20°C: shows little or no damage after 30 days.
LDPE at 50°C: shows damage and is not recommended.
ChlorobenzeneImmediate damage may occur.
Not recommended for continuous use.
ChloroformLDPE / HDPE at 20°C: show some effect after 7 days.
LDPE / HDPE at 50°C: immediate damage may occur.
Not recommended for continuous use.
Chromic acid 10%LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Chromic acid 50%LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Citric acid 10%LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
CresolHDPE at 20°C: shows some effect after 7 days.
LDPE at 20°C-50°C & HDPE at 50°C: show immediate damage.
Not recommended for continuous use.
CyclohexaneLDPE / HDPE at 50°C: immediate damage may occur.
LDPE / HDPE at 20°C: show some effect after 7 days.
Diethyl ketoneLDPE / HDPE at 20°C-50°C: damage may occur.
Not recommended for continuous use.
DimethylsulfoxideLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ethanol 95%LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ethyl acetateLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ethyl benzeneHDPE at 20°C: shows some effect after 7 days.
LDPE at 20°C-50°C & HDPE at 50°C: show immediate damage.
Not recommended for continuous use.
Ethylene glycolLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ethylene oxideHDPE at 20°C: shows little or no damage after 30 days.
LDPE at 20°C: and LDPE/ HDPE at 50°C: show some effect after 7 days.
Ferric chlorideLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
FluorideLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
FluorineHDPE at 20°C: shows little or no damage after 30 days.
LDPE at 20°C: shows some effect after 7 days.
Not recommended at 50°C.
Formaldehyde 10%LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Formaldehyde 40%LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
GlycerolLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
HexaneHDPE at 20°C: shows little or no damage after 30 days continuous use.
HDPE at 50 °C: shows some effect after 7 days.
LDPE not recommended at any temperature.
Hydrochloric acid 20%LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrochloric acid 35%LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrochloric acid 5%LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrocyanic acidLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrofluoric acidLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrofluoric acid 4%LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrofluoric acid 48%LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrogen peroxide 3%LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrogen peroxide 30%LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Isobutyl alcoholLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Isopropyl alcoholLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
KeroseneLDPE / HDPE at 20°C: show some effect after 7 days.
LDPE / HDPE not recommended at 50°C, as immediate damage may occur.
Lactic Acid 10 %LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Lactic Acid 90 %LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Lead acetateLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
MethanolLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Methyl ethyl ketoneImmediate damage may occur.
Not recommended for continuous use.
Methyl propyl ketoneHDPE at 20°C: shows some effect after 7 days.
LDPE at 20°C-50°C & HDPE at 50°C: Immediate damage may occur.
Not recommended for continuous use.
Methylene chlorideHDPE at 20°C: shows some effect after 7 days.
LDPE at 20°C-50°C & HDPE at 50°C: Immediate damage may occur.
Not recommended for continuous use.
Mineral oilLDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE at 50°C: may show immediate damage and is not recommended.
n-amyl acetateLDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE at 50°C: shows some effect after 7 days or constant exposure.
n-butyl alcoholLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Nitric acid 50 %LDPE at 20°C: shows little or damage after 30 days.
HDPE at 20°C & LDPE at 50°C: show effect after 7 days.
HDPE at 50°C: shows immediate damage and is not recommended.
Nitric acid 70 %LDPE / HDPE at 20°C: show some effect after 7 days.
LDPE / HDPE at 50°C: show immediate damage.
Not recommended.
n-octaneLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Oleic acidHDPE at 20°C-50°C: little or no damage after 30 days.
LDPE at 20°C-50°C: shows immediate damage and is not recommended.
Oxalic acidLDPE at 20°C: shows some effect after 7 days.
HDPE at 20°C and LDPE / HDPE at 50°C: shows little/ no damage after 30 days.
OzoneLDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE / HDPE at 50°C: show immediate damage.
Not recommended.
Perchloric acidLDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE / HDPE at 50°C: show immediate damage.
Not recommended.
Perchloric ethyleneLDPE / HDPE at 20°C-50°C: show immediate damage.
Not recommended.
PhenolLDPE / HDPE at 20°C-50°C: show immediate damage.
Not recommended.
Phosphoric acid 10%LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Phosphoric acid 85%LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE at 50°C: shows immediate damage and is not recommended.
Phosphorous trichlorideLDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE at 50°C: has no data available. HDPE at 50°C: shows some effect after 7 days.
Potassium carbonateLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Potassium hydroxide 5 %LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Potassium hydroxide concentratedLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Potassium permanganateLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Propylene glycolLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
PyridineImmediate damage may occur.
Not recommended for continuous use.
Salicylic acid, saturatedLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Silver acetateLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Silver nitrateLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sodium carbonateLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sodium chloride, saturatedLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sodium dichromateLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sodium hydroxide 1%LDPE at 20°C-50°C: shows little or no damage after 30 days.
HDPE at 20°C-50°C: shows some effect after 7 days.
Sodium hydroxide 50%LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sodium hypochlorite 15%HDPE at 20°C-50°C: little or no damage after 30 days.
LDPE at 20°C: is suitable
but at 50°C: shows some effect after 7 days.
Sodium nitrateLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sodium sulphateLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
SucroseLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sulfuric acid 20%LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sulfuric acid 6%LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sulfuric acid 60%LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sulfuric acid 98%LDPE at 20°C-50°C: shows little or no damage after 30 days.
HDPE at 20°C: shows effect after 7 days.
Not recommended for use at 50°C.
Tannic acidLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
TetrahydrofuranLDPE / HDPE at 20°C: show some effect after 7 day of constant exposure.
LDPE / HDPE at 50°C: show immediate damage.
Not recommended.
TolueneLDPE at 20°C: show some effect after 7 day of constant exposure.
HDPE at 20°C-50°C & LDPE at 50°C: show immediate damage.
Not recommended.
Trichloracetic acidLDPE / HDPE at 20°C: show some effect after 7 day of constant exposure.
LDPE / HDPE at 50°C: show immediate damage.
Not recommended.
TrichlorethaneImmediate damage may occur.
Not recommended for continuous use.
Turpentine oilLDPE / HDPE at 20°C: show some effect after 7 days.
LDPE / HDPE at 50°C: show immediate damage.
Not recommended.
UreaLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
XyleneHDPE at 20°C: shows some effect after 7 day of constant exposure.
LDPE at 20-50°C and HDPE at 50°C: show immediate damage.
Not recommended.
Zinc chlorideLDPE / HDPE at 20°C-50°C: little or no damage after 30 days.

Send your message to this supplier

*From:
*To:
avatar Mr. Tom King
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

Find Similar Products By Category

Supplier Homepage Products Storage Tank Steel Lined Plastic LLDPE Spray Tower Tank for Chemical Corrosion Resistant (Desulfurization, Acid washing, Wast Gas Treatment)