13200 Gallon Hydrochloric Acid Storage PE Tank (Vertical/Horizontal LLDPE Tank Sodium Hypochlorite, HCl Acid 10566Gal, 7925Gal, 5283Gal, 3962Gal, 2641Gal)

• After-sales Service: 24
• Warranty: 24
• Condition: New
• Customized: Customized
• Certification: ISO9001, GB
• Tank Marerial: Metal Tank
• Model NO.: PE Tank
• Type: Horizontal / Vertical
• Storage Objects: Liquid, Gas
• Materical: Q235A + PE (Plastic )16mm -22mm
• Type H: Horizontal / Vertical
• Transport Package: Nil
• Specification: OEM
• Trademark: Dong Run Ze
• Origin: China
• HS Code: 73090000
• Production Capacity: 8000

Product Description

13200 Gallon Hydrochloric Acid Storage PE Tank (Vertical/Horizontal LLDPE Tank Sodium Hypochlorite,HCL Acid 10566Gal,7925Gal,5283Gal,3962Gal,2641Gal ) 
  Steel Lined Plastic LLDPE  Vertical Flat Bottom Steel Lined Plastic LLDPE Tank For  Storage HCl (max 35%) , Naoh (max 50%) , Naclo (max 10%)
Electrolytic Polishing Tank / Can /Pool Pipe Unit, Electrolytic Cleaning Tank,Acid Polishing Tank

Hydrochloric Acid Plastic Storage Tank, Hydrochloric Acid Polyethylene Storage Tank, Hydrochloric Acid LLDPE Storage Tank, Hydrochloric Acid Vertical Storage Tank


Metal cans Steel-Lined Plastic Square Tank, Electrolytic Tank, Pickling Tank  Acid Containment Vessels Custom Made Rotationally Molded Linear Resins LLDPE
Custermizing Checmial Acid Storage Tank 1-150 m3 Steel Lined LLDPE  Tank Used to Contain: HCl (max 35%) , Naoh (max 50%) , Naclo (max 10%) , PAC (max 17%) ,H2so4  

Used to contain: HCl (max 35%), NaOH (max 50%), NaCLO (max 10%), PAC (max 17%), H2SO4 etc 

 Media (density) : (1155 Kg/m3), Hydrochloric Acid (1150 Kg/m3), Sulfate, Nitrate (1152 Kg/m3), Phosphate (1151 Kg/m3), Hydrofluoric Acid (1132 Kg/m3), Battery Fluid (1135 Kg/m3), Chloride (1135 Kg/m3), Ferric Chloride Solution (1130 Kg/m3), Sodium Hypochlorite (1130 Kg/m3), Sulfurous Acid (1030 Kg/m3)

processing/storing; aluminum sulfate, ammonium sulfate, calcium chloride, ethylene glycol, ferric chloride, ferric sulfate, ferrous sulfate, hydrochloric acid, hydrofluoric acid, hydrofluosilicic acid, hydrogen peroxide, magnesium chloride, phosphoric acid, polymers, potassium hydroxide, or just plain water and we'll design the vessel(s) you require.

Horizontal / Vertical Storage HCL Acid Tanks Steel Lined LDPE  
For Storage Bleach, Hydrochloric Acid, Ferric Chloride, Oilfield Chemicals, Corrosive Wastes And Other Hazardous Cargoes. 
Steel ( 6 mm -8mm ) Lined PE Plastic 7042 (16mm - 25 mm ) storage tank 

Steel Lined LDPE aslo for Steel Lined LDPE Tank aslo for HCL(max 35%), NaOH (max 50%), NaCLO (max 10%), PAC (max 17%),H2SO4(60%,98%) ,HF (48%),H3PO4 (10%-85%),NH3. H2O,H2O2 (30%) Hazardous LiquidsTank Container 

  Steel Lined LDPE aslo for HCL(max 35%), NaOH (max 50%), NaCLO (max 10%), PAC (max 17%),H2SO4(60%,98%) ,HF ( 48%),H3PO4 (10%-85%),NH3. H2O,H2O2 (30%) 
Compounds, cleaning liquid, UN1760,  
Corrosive liquid, acidic, inorganic, n.o.s., UN3264,  
Corrosive liquid, acidic, organic, n.o.s., UN3265,  
Corrosive liquid, basic, inorganic, n.o.s., UN3266,  
Hypochlorite solutions, UN1791,  
Hydrochloric acid solution, UN1789,  
Sulfuric acid, UN2796,   
BATTERY FLUID, ALKALI UN 2797,Vertical type PE  Plastic  tank price for refer

Capaicty	Shell length	Total length	Diameter	Weight	Shell thickness	EXW Price
1m3	750 mm	930 mm	1300 mm	95(KG)	15 mm	$1355~$2060
2m3	1800 mm	1980 mm	1300 mm	150(KG)	15 mm	$1565~$2260
5m3	1100 mm	1400 mm	2400 mm	260(KG)	15 mm	$1880~$2560
10m3	2200 mm	2500 mm	2400 mm	500(KG)	20 mm	$2508~$3560
15m3	3300 mm	3600 mm	2400 mm	680(KG)	20 mm	$3850~$5560
20m3	4400 mm	4700 mm	2400 mm	850(KG)	22 mm	$5480~$7180
30m3	4400 mm	5040 mm	3000 mm	1350(KG)	25 mm	$6490~$8190
40m3	4900 mm	5500 mm	3450 mm	2000(KG)	32 mm	$6860~$8560
50m3	6000 mm	6600 mm	3450 mm	2300(KG)	32 mm	$11520~$13920

5 cbm/m3	Q235A 5mm+ PE  (Plastic )16mm	US$7,200.00
10 m3	Q235A 5mm+PE16mm	US$9,200.00
20 m3	Q235A 5mm+PE16mm	US$11,200.00
30	Q235A 6mm+PE16mm	US$13,200.00
40	Q235A 6mm+PE16mm	US$15,200.00
50	Q235A 6mm+PE16mm	US$17,200.00
60	Q235A 6mm+PE16mm	US$19,200.00
70	Q235A 6mm+PE16mm	US$21,200.00
80	Q235A 8mm+PE16mm	US$23,200.00
90	Q235A 8mm+PE16mm	US$25,200.00
100	Q235A 8mm+PE16mm	US$27,200.00
110	Q235A 8mm+PE16mm	US$29,200.00
120	Q235A 8mm+PE16mm	US$30,800.00
130	Q235A 8mm+PE16mm	US$32,400.00
135	Q235A 8mm+PE16mm	US$34,400.00

                                Price for refer                                                                     

Detail Picture

Vertical Hydrochloric Acid Storage Tanks ,Dosing tank, Day tank 30cbm  (30000L) Draft 
Vertical Bleach  Sodium Hypochlorite ,Acid Storage Dosing Tanks 10cbm  (10000L) Draft 
Vertical Bleach  Sodium Hypochlorite ,Acid Dosing Tanks , measuring tank 5m3  (5000L) Draft 
Vertical Bleach  Sodium Hypochlorite ,Acid Dosing Tanks , measuring tank 2m3  (2000L) Draft 
metering tank
Vertical Hydrochloric Acid Storage Tanks 50cbm  (50000L) Draft 
Vertical Hydrochloric Acid Storage Tanks 30cbm (30000L) Draft 
Vertical Hydrochloric Acid Storage Tanks 15cbm (15000L) Draft 
Vertical Hydrochloric Acid Storage Tanks 10cbm (10000L) Draft 
Vertical Hydrochloric Acid Storage Tanks 5000L Draft 
 
Rotationally Molded LLDPE TANK
 chemical resistance of LLDPE    
 tictrucks.en.made-in-china.com   
Acid Storage Tank

Certifications

Packaging & Shipping

LDPE / HDPE Chemical Resistance Chart 

The chemical compatibility of LDPE and HDPE on this chart is tested at 20°C: and 50°C: for 7 days and 30 days (if applicable) with constant exposure.

LDPE & HDPE resistance listed by chemical
1.4-dioxane	LDPE / HDPE at 20°C: little or no damage after 30 days. LDPE at 50°C: shows some effect after 7 days.
Acetaldehyde	LDPE / HDPE at 20°C: little or no damage after 30 days. HDPE at 50°C: shows some effect after 7 days. LDPE at 50°C: immediate damage may occur.
Acetic Acid 5 %	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Acetic Acid, glacial 50%	LDPE / HDPE at 20°C: little or no damage after 30 days. LDPE at 50 °C: immediate damage may occur.
Acetone	LDPE / HDPE at 20°C-50°C: damage may occur. Not recommended for continuous use.
Allyl Alcohol	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Aluminum salts	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Amino acids	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ammonia	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ammonium carbonate saturated	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ammonium phosphate	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ammonium sulphate	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Amyl chloride	HDPE at 20°C: shows some effect after 7 days. HDPE at 50°C & LDPE at 20°C-50°C: immediate damage may occur. Not recommended for continuous use.
Aniline	LDPE / HDPE at 20°C: little or no damage after 30 days. HDPE at 50°C: shows some effect after 7 days.
Benzene	LDPE / HDPE at 20°C-50°C: damage may occur. Not recommended for continuous use.
Benzyl alcohol	LDPE / HDPE at 50°C: immediate damage may occur. HDPE at 20°C: shows some effect after 7 days.
Boric acid	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Bromine	LDPE / HDPE at 50°C: immediate damage may occur. HDPE at 20°C: shows some effect after 7 days.
Butyric acid	LDPE / HDPE at 50°C: immediate damage may occur. HDPE at 20°C: shows some effect after 7 days.
Calcium chloride	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Calcium hydroxide saturated	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Carbon tetrachloride	HDPE at 20°C: shows little or no damage after 30 days. LDPE at 20°C & HDPE at 50°C: show some effect after 7 days. LDPE at 50°C: not recommended.
Chlorine 10% in water	LDPE / HDPE at 20°C: shows little or no damage after 30 days. LDPE at 50°C: shows damage and is not recommended.
Chlorobenzene	Immediate damage may occur. Not recommended for continuous use.
Chloroform	LDPE / HDPE at 20°C: show some effect after 7 days. LDPE / HDPE at 50°C: immediate damage may occur. Not recommended for continuous use.
Chromic acid 10%	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Chromic acid 50%	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Citric acid 10%	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Cresol	HDPE at 20°C: shows some effect after 7 days. LDPE at 20°C-50°C & HDPE at 50°C: show immediate damage. Not recommended for continuous use.
Cyclohexane	LDPE / HDPE at 50°C: immediate damage may occur. LDPE / HDPE at 20°C: show some effect after 7 days.
Diethyl ketone	LDPE / HDPE at 20°C-50°C: damage may occur. Not recommended for continuous use.
Dimethylsulfoxide	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ethanol 95%	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ethyl acetate	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ethyl benzene	HDPE at 20°C: shows some effect after 7 days. LDPE at 20°C-50°C & HDPE at 50°C: show immediate damage. Not recommended for continuous use.
Ethylene glycol	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ethylene oxide	HDPE at 20°C: shows little or no damage after 30 days. LDPE at 20°C: and LDPE/ HDPE at 50°C: show some effect after 7 days.
Ferric chloride	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Fluoride	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Fluorine	HDPE at 20°C: shows little or no damage after 30 days. LDPE at 20°C: shows some effect after 7 days. Not recommended at 50°C.
Formaldehyde 10%	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Formaldehyde 40%	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Glycerol	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hexane	HDPE at 20°C: shows little or no damage after 30 days continuous use. HDPE at 50 °C: shows some effect after 7 days. LDPE not recommended at any temperature.
Hydrochloric acid 20%	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrochloric acid 35%	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrochloric acid 5%	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrocyanic acid	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrofluoric acid	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrofluoric acid 4%	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrofluoric acid 48%	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrogen peroxide 3%	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrogen peroxide 30%	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Isobutyl alcohol	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Isopropyl alcohol	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Kerosene	LDPE / HDPE at 20°C: show some effect after 7 days. LDPE / HDPE not recommended at 50°C, as immediate damage may occur.
Lactic Acid 10 %	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Lactic Acid 90 %	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Lead acetate	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Methanol	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Methyl ethyl ketone	Immediate damage may occur. Not recommended for continuous use.
Methyl propyl ketone	HDPE at 20°C: shows some effect after 7 days. LDPE at 20°C-50°C & HDPE at 50°C: Immediate damage may occur. Not recommended for continuous use.
Methylene chloride	HDPE at 20°C: shows some effect after 7 days. LDPE at 20°C-50°C & HDPE at 50°C: Immediate damage may occur. Not recommended for continuous use.
Mineral oil	LDPE / HDPE at 20°C: little or no damage after 30 days. LDPE at 50°C: may show immediate damage and is not recommended.
n-amyl acetate	LDPE / HDPE at 20°C: little or no damage after 30 days. LDPE at 50°C: shows some effect after 7 days or constant exposure.
n-butyl alcohol	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Nitric acid 50 %	LDPE at 20°C: shows little or damage after 30 days. HDPE at 20°C & LDPE at 50°C: show effect after 7 days. HDPE at 50°C: shows immediate damage and is not recommended.
Nitric acid 70 %	LDPE / HDPE at 20°C: show some effect after 7 days. LDPE / HDPE at 50°C: show immediate damage. Not recommended.
n-octane	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Oleic acid	HDPE at 20°C-50°C: little or no damage after 30 days. LDPE at 20°C-50°C: shows immediate damage and is not recommended.
Oxalic acid	LDPE at 20°C: shows some effect after 7 days. HDPE at 20°C and LDPE / HDPE at 50°C: shows little/ no damage after 30 days.
Ozone	LDPE / HDPE at 20°C: little or no damage after 30 days. LDPE / HDPE at 50°C: show immediate damage. Not recommended.
Perchloric acid	LDPE / HDPE at 20°C: little or no damage after 30 days. LDPE / HDPE at 50°C: show immediate damage. Not recommended.
Perchloric ethylene	LDPE / HDPE at 20°C-50°C: show immediate damage. Not recommended.
Phenol	LDPE / HDPE at 20°C-50°C: show immediate damage. Not recommended.
Phosphoric acid 10%	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Phosphoric acid 85%	LDPE / HDPE at 20°C: little or no damage after 30 days. LDPE at 50°C: shows immediate damage and is not recommended.
Phosphorous trichloride	LDPE / HDPE at 20°C: little or no damage after 30 days. LDPE at 50°C: has no data available. HDPE at 50°C: shows some effect after 7 days.
Potassium carbonate	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Potassium hydroxide 5 %	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Potassium hydroxide concentrated	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Potassium permanganate	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Propylene glycol	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Pyridine	Immediate damage may occur. Not recommended for continuous use.
Salicylic acid, saturated	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Silver acetate	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Silver nitrate	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sodium carbonate	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sodium chloride, saturated	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sodium dichromate	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sodium hydroxide 1%	LDPE at 20°C-50°C: shows little or no damage after 30 days. HDPE at 20°C-50°C: shows some effect after 7 days.
Sodium hydroxide 50%	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sodium hypochlorite 15%	HDPE at 20°C-50°C: little or no damage after 30 days. LDPE at 20°C: is suitable but at 50°C: shows some effect after 7 days.
Sodium nitrate	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sodium sulphate	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sucrose	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sulfuric acid 20%	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sulfuric acid 6%	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sulfuric acid 60%	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sulfuric acid 98%	LDPE at 20°C-50°C: shows little or no damage after 30 days. HDPE at 20°C: shows effect after 7 days. Not recommended for use at 50°C.
Tannic acid	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Tetrahydrofuran	LDPE / HDPE at 20°C: show some effect after 7 day of constant exposure. LDPE / HDPE at 50°C: show immediate damage. Not recommended.
Toluene	LDPE at 20°C: show some effect after 7 day of constant exposure. HDPE at 20°C-50°C & LDPE at 50°C: show immediate damage. Not recommended.
Trichloracetic acid	LDPE / HDPE at 20°C: show some effect after 7 day of constant exposure. LDPE / HDPE at 50°C: show immediate damage. Not recommended.
Trichlorethane	Immediate damage may occur. Not recommended for continuous use.
Turpentine oil	LDPE / HDPE at 20°C: show some effect after 7 days. LDPE / HDPE at 50°C: show immediate damage. Not recommended.
Urea	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Xylene	HDPE at 20°C: shows some effect after 7 day of constant exposure. LDPE at 20-50°C and HDPE at 50°C: show immediate damage. Not recommended.
Zinc chloride	LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.