| Specification | General PTFE thickness and negative pressure-resistance | The thickness of PTFE wall required to resist-0.1MPA pressure when the temperature is less than 120degree, | |
| DN25 | 2mm | -0.08Mpa | 3mm(L≤3000mm) |
| DN32 | 2mm | -0.075Mpa | 3mm(L≤3000mm) |
| DN40 | 2.5mm | -0.075Mpa | 4mm(L≤3000mm) |
| DN50 | 2.5mm | -0.06Mpa | 5mm(L≤3000mm) |
| DN65 | 2.5mm | -0.05Mpa | 8mm(L≤1000mm) |
| DN80 | 3mm | -0.05Mpa | 10mm(L≤1000mm) |
| DN100 | 3mm | -0.04Mpa | 13mm(L≤1000mm) |
| DN125 | 4mm | -0.03Mpa | 13mm(L≤1000mm) |
| DN150 | 4mm | -0.025Mpa | 13mm(L≤1000mm) |
| DN200 | 5mm | -0.02Mpa | 15mm(L≤1000mm) |
| PTFE lined 90° elbow | Unit mm | ||||||||
| Nominal diameter | Specification of balled iron T | Raised face A | Central height C1 | Inside diameter D1 | PTFE thickness | out side diameter of flange D | Diameter of bolt circle K | Thickness of flange C | |
| DN(mm) | NPS(inch) | ||||||||
| DN15 | 1/2 | 34 | 40 | 80 | 15 | 5 | 90 | 65 | 11 |
| DN20 | 3/4 | 38 | 45 | 90 | 18 | 5 | 100 | 75 | 11 |
| DN25 | 1 | 42 | 60 | 92 | 22 | 5 | 110 | 85 | 12 |
| DN32 | 1 1/4 | 48 | 70 | 100 | 28 | 5 | 130 | 100 | 13 |
| DN40 | 1 1/2 | 57 | 80 | 112 | 38 | 5 | 140 | 110 | 14 |
| DN50 | 2 | 68 | 95 | 117 | 48 | 5 | 155 | 125 | 14 |
| DN65 | 2 1/2 | 89 | 115 | 135 | 63 | 8 | 175 | 145 | 16 |
| DN80 | 3 | 108 | 130 | 150 | 78 | 8 | 190 | 160 | 16 |
| DN100 | 4 | 114 | 150 | 150 | 87 | 8 | 210 | 180 | 18 |
| DN125 | 5 | 140 | 180 | 190 | 110 | 8 | 240 | 210 | 20 |
| DN150 | 6 | 168 | 205 | 230 | 135 | 10 | 275 | 240 | 20 |
| DN200 | 8 | 219 | 260 | 305 | 180 | 10 | 330 | 295 | 20 |
| DN250 | 10 | 273 | 315 | 380 | 230 | 12 | 385 | 350 | 23 |
| DN300 | 12 | 325 | 365 | 420 | 280 | 12 | 435 | 400 | 23 |
Customizing Chemical Reactor Tank Lined LDPE OR PTFE F4 (Mixing Vessel Reactor/Heat Exchanger/Condenser/ Storage Receiver/ Mixer Tank)
Key words:
| ptfe lined pipe fittings | ptfe lined tee | ptfe lined reducer | ptfe lined elbow | ptfe lined cross |
| ptfe lined pipe and fittings | ptfe lined90degree elbow | ptfe lined 45 degrdd elbow | ptfe lined ECC reducer | ptfe lined CON reducer |
| ptfe lined equal tee | ptfe lined reduce tee | ptfe lined unequal tee | ptfe lined pipe | ptfe lined fittings |
| ptfe lined carbon steel pipe fittings | ptfe lined carbon steel tee | ptfe lined carbon steel reducer | ptfe lined carbon steel elbow | ptfe lined carbon steel cross |
| PTFE pipe | PTFE lined pipe(Australia) | Resistant Stainless Steel Pipe | Resistant Steel Pipe | Carbon seamless steel pipe |
| Anti Corrosion Pipe Fittings Lined | PTFE lining fittings | PTFE lined piping | straight tee | PTFE lined bends |
|
PTFE Lined Pipe (with fixed or rotation flange) |
0 Professional China Supplier of Glass Lined Pipe for Corrosion Resistance Manufacturer of PTFE Flexible Connector Resistance PTFE Lined Pipe High-Quality PE Lined Corrosion Resistance Tee High Corrosion China Made High-Quality PFA Lined Ball Valve |
High Corrosion Resistance PTFE Lined Pipe FOB Price: US $500 / Piece Min. Order: 10 Meters FEP Lined Butterfly Valve D941 (D941) FEP Lined Butterfly Valve D941 (D941) Min. Order: 10 Pieces FEP Lined Butterfly Valve D41 FEP Lined Butterfly Valve D41 Min. Order: 10 Pieces FEP Lined Butterfly Valve D671 FEP Lined Butterfly Valve D671 Min. Order: 10 Pieces FEP Lined Butterfly Valve D71 FEP Lined Butterfly Valve D71 Min. Order: 10 Pieces Professional China Supplier of PTFE Lined Check Valve (H42) Professional China Supplier of PTFE Lined Check Valve (H42) Min. Order: 10 Pieces FEP Lined Check Valve FEP Lined Check Valve Min. Order: 1 Piece PTFE Lined Baiting Ball Valve PTFE Lined Baiting Ball Valve FOB Price: US $10-1,000 / Piece Min. Order: 1 Piece PFA Lined Ball Valve (FK) PFA Lined Ball Valve (FK) FOB Price: US $500-10,000 / Piece Min. Order: 1 Piece FEP Lined Ball Valve (Q941) FEP Lined Ball Valve (Q941) FOB Price: US $10-1,000 / Piece Min. Order: 1 Piece FEP Lined Ball Valve (Q641) FEP Lined Ball Valve (Q641) FOB Price: US $200-1,000 / Piece Min. Order: 1 Piece Wcb Flange Ball Valve Pn16, 150lb, 300lb Wcb Flange Ball Valve Pn16, 150lb, 300lb FOB Price: US $200-1,000 / Piece Min. Order: 1 Piece PTFE Lined DIP Pipe/Feeding Pipe/Entry Pipe PTFE Lined DIP Pipe/Feeding Pipe/Entry Pipe FOB Price: US $50 / Piece Min. Order: 1 Piece PTFE Lined Tank Horizontal Pressure Vessels PTFE Lined Tank Horizontal Pressure Vessels Min. Order: 1 Piece PTFE Lined Columns PTFE Lined Columns Min. Order: 1 Piece ETFE Line Pipe ETFE Line Pipe Min. Order: 1 Piece PTFE Lined Butterfly Valve PTFE Lined Butterfly Valve Min. Order: 1 Piece Expansion Joint From China for Sell Expansion Joint From China for Sell FOB Price: US $600 / Piece Min. Order: 1 Piece Butterfly Valve Butterfly Valve Min. Order: 1 Piece PTFE Lined Reactor PTFE Lined Reactor Min. Order: 1 Piece Butterfly Valve Butterfly Valve Min. Order: 1 Piece PTFE Lined Vessel PTFE Lined Vessel Min. Order: 1 Piece Butterfly Valve Butterfly Valve Min. Order: 10 Pieces Vacuum Resistance PTFE Expansion Joint Vacuum Resistance PTFE Expansion Joint Min. Order: 1 Piece Rubber Expansion Joint with PTFE Lining Rubber Expansion Joint with PTFE Lining Min. Order: 10 Pieces PTFE Bellows to Compensate for Mechanical and Thermal Changes PTFE Bellows to Compensate for Mechanical and Thermal Changes Min. Order: 1 Piece PTFE Expansion Joint for Normal Pressure 0.1mpa PTFE Expansion Joint for Normal Pressure 0.1mpa Min. Order: 1 Piece PTFE Lined Cross for Chemical Plants PTFE Lined Cross for Chemical Plants FOB Price: US $250 / Piece Min. Order: 10 Pieces Plastic Lined Equal Tee (carbon steel) Plastic Lined Equal Tee (carbon steel) FOB Price: US $500 / Piece Min. Order: 10 Pieces Expansion Rubber Bellow Flange Expansion Rubber Bellow Flange FOB Price: US $500 / Piece Min. Order: 1 Piece PTFE Lined Cross PTFE Lined Cross FOB Price: US $250 / Piece Min. Order: 10 Pieces PTFE/Teflon Lined Tee (Equal tee) PTFE/Teflon Lined Tee (Equal tee) FOB Price: US $200 / Piece Min. Order: 1 Piece Plastic Lined Pipe Plastic Lined Pipe Min. Order: 10 Meters Plastic Lined Elbow (OEM service supplied) Plastic Lined Elbow (OEM service supplied) FOB Price: US $200 / Piece Min. Order: 10 PiecesTeflon Lined Reducer FOB Price: US $200 / Piece Min. Order: 1 Piece Jacketed Glass Lined Reactor 10000L Supplier From China Jacketed Glass Lined Reactor 10000L Supplier From China Min. Order: 1 Piece Horizontal Glass Lined Storage Tank Horizontal Glass Lined Storage Tank FOB Price: US $200-20,000 / Piece Min. Order: 1 Piece Glass Lined Elbow 45deg Glass Lined Elbow 45deg Min. Order: 1 Piece Metallic Expansion Joints Metallic Expansion Joints FOB Price: US $40 / Piece Min. Order: 10 Pieces Professional China Supplier of PTFE Pipe Professional China Supplier of PTFE Pipe Min. Order: 10 Meters Professional China Glass Lined Falling Film Evaporator Professional China Glass Lined Falling Film Evaporator FOB Price: US $10,000 / set Min. Order: 1 set PP/Po/PE Lined Pipe and Fittings PP/Po/PE Lined Pipe and Fittings Min. Order: 10 Pieces Professional China Supplier of Glass Lined Plate Condenser Professional China Supplier of Glass Lined Plate Condenser Min. Order: 1 Piece Cast Steel and Stainless Steel FEP Lined Globe Valve Cast Steel and Stainless Steel FEP Lined Globe Valve Min. Order: 1 Piece Professional China Supplier of PFA Lined Ball Valve Professional China Supplier of PFA Lined Ball Valve FOB Price: US $500-10,000 / Piece Min. Order: 1 Piece PTFE Lined Insulation Ball Valve PTFE Lined Insulation Ball Valve Min. Order: 10 Pieces FEP/PFA/E-Tfe/PTFE Lined Ball Valve FEP/PFA/E-Tfe/PTFE Lined Ball Valve Min. Order: 10 Pieces Guaranteed PTFE Corrugated Flexible Hose Guaranteed PTFE Corrugated Flexible Hose FOB Price: US $10-500 / Piece Min. Order: 1 Piece Professional Manufacturer of PTFE Lined Sight Glass Professional Manufacturer of PTFE Lined Sight Glass Min. Order: 1 Piece PTFE/FEP/PFA/E-Tfe Lined Butterfly Valve PTFE/FEP/PFA/E-Tfe Lined Butterfly Valve Min. Order: 10 Pieces Professional China Supplier of FEP Lined Check Valve Professional China Supplier of FEP Lined Check Valve Min. Order: 1 Piece China Made PTFE Gasket China Made PTFE Gasket FOB Price: US $10-200 / Piece Min. Order: 100 Pieces Zy212 Mechanical Seal Zy212 Mechanical Seal Min. Order: 10 Pieces Zy212b Mechanical Seal Zy212b Mechanical Seal Min. Order: 10 Pieces Professional China Manufacturer of Zy204b Mechanical Seal Professional China Manufacturer of Zy204b Mechanical Seal Min. Order: 1 Piece Zy205/206/207 Mechanical Seal for Industrial Pump Zy205/206/207 Mechanical Seal for Industrial Pump Min. Order: 10 Pieces Zy2009 Mechanical Seal for Reactors Zy2009 Mechanical Seal for Reactors Min. Order: 10 Pieces High-Quality PP Lined Corrosion Resistance Pipe |
The chemical compatibility of LDPE and HDPE on this chart is tested at 20°C: and 50°C: for 7 days and 30 days (if applicable) with constant exposure.
| LDPE & HDPE resistance listed by chemical | |
| 1.4-dioxane | LDPE / HDPE at 20°C: little or no damage after 30 days. LDPE at 50°C: shows some effect after 7 days. |
| Acetaldehyde | LDPE / HDPE at 20°C: little or no damage after 30 days. HDPE at 50°C: shows some effect after 7 days. LDPE at 50°C: immediate damage may occur. |
| Acetic Acid 5 % | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Acetic Acid, glacial 50% | LDPE / HDPE at 20°C: little or no damage after 30 days. LDPE at 50 °C: immediate damage may occur. |
| Acetone | LDPE / HDPE at 20°C-50°C: damage may occur. Not recommended for continuous use. |
| Allyl Alcohol | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Aluminum salts | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Amino acids | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Ammonia | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Ammonium carbonate saturated | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Ammonium phosphate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Ammonium sulphate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Amyl chloride | HDPE at 20°C: shows some effect after 7 days. HDPE at 50°C & LDPE at 20°C-50°C: immediate damage may occur. Not recommended for continuous use. |
| Aniline | LDPE / HDPE at 20°C: little or no damage after 30 days. HDPE at 50°C: shows some effect after 7 days. |
| Benzene | LDPE / HDPE at 20°C-50°C: damage may occur. Not recommended for continuous use. |
| Benzyl alcohol | LDPE / HDPE at 50°C: immediate damage may occur. HDPE at 20°C: shows some effect after 7 days. |
| Boric acid | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Bromine | LDPE / HDPE at 50°C: immediate damage may occur. HDPE at 20°C: shows some effect after 7 days. |
| Butyric acid | LDPE / HDPE at 50°C: immediate damage may occur. HDPE at 20°C: shows some effect after 7 days. |
| Calcium chloride | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Calcium hydroxide saturated | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Carbon tetrachloride | HDPE at 20°C: shows little or no damage after 30 days. LDPE at 20°C & HDPE at 50°C: show some effect after 7 days. LDPE at 50°C: not recommended. |
| Chlorine 10% in water | LDPE / HDPE at 20°C: shows little or no damage after 30 days. LDPE at 50°C: shows damage and is not recommended. |
| Chlorobenzene | Immediate damage may occur. Not recommended for continuous use. |
| Chloroform | LDPE / HDPE at 20°C: show some effect after 7 days. LDPE / HDPE at 50°C: immediate damage may occur. Not recommended for continuous use. |
| Chromic acid 10% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Chromic acid 50% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Citric acid 10% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Cresol | HDPE at 20°C: shows some effect after 7 days. LDPE at 20°C-50°C & HDPE at 50°C: show immediate damage. Not recommended for continuous use. |
| Cyclohexane | LDPE / HDPE at 50°C: immediate damage may occur. LDPE / HDPE at 20°C: show some effect after 7 days. |
| Diethyl ketone | LDPE / HDPE at 20°C-50°C: damage may occur. Not recommended for continuous use. |
| Dimethylsulfoxide | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Ethanol 95% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Ethyl acetate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Ethyl benzene | HDPE at 20°C: shows some effect after 7 days. LDPE at 20°C-50°C & HDPE at 50°C: show immediate damage. Not recommended for continuous use. |
| Ethylene glycol | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Ethylene oxide | HDPE at 20°C: shows little or no damage after 30 days. LDPE at 20°C: and LDPE/ HDPE at 50°C: show some effect after 7 days. |
| Ferric chloride | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Fluoride | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Fluorine | HDPE at 20°C: shows little or no damage after 30 days. LDPE at 20°C: shows some effect after 7 days. Not recommended at 50°C. |
| Formaldehyde 10% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Formaldehyde 40% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Glycerol | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Hexane | HDPE at 20°C: shows little or no damage after 30 days continuous use. HDPE at 50 °C: shows some effect after 7 days. LDPE not recommended at any temperature. |
| Hydrochloric acid 20% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Hydrochloric acid 35% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Hydrochloric acid 5% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Hydrocyanic acid | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Hydrofluoric acid | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Hydrofluoric acid 4% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Hydrofluoric acid 48% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Hydrogen peroxide 3% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Hydrogen peroxide 30% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Isobutyl alcohol | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Isopropyl alcohol | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Kerosene | LDPE / HDPE at 20°C: show some effect after 7 days. LDPE / HDPE not recommended at 50°C, as immediate damage may occur. |
| Lactic Acid 10 % | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Lactic Acid 90 % | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Lead acetate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Methanol | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Methyl ethyl ketone | Immediate damage may occur. Not recommended for continuous use. |
| Methyl propyl ketone | HDPE at 20°C: shows some effect after 7 days. LDPE at 20°C-50°C & HDPE at 50°C: Immediate damage may occur. Not recommended for continuous use. |
| Methylene chloride | HDPE at 20°C: shows some effect after 7 days. LDPE at 20°C-50°C & HDPE at 50°C: Immediate damage may occur. Not recommended for continuous use. |
| Mineral oil | LDPE / HDPE at 20°C: little or no damage after 30 days. LDPE at 50°C: may show immediate damage and is not recommended. |
| n-amyl acetate | LDPE / HDPE at 20°C: little or no damage after 30 days. LDPE at 50°C: shows some effect after 7 days or constant exposure. |
| n-butyl alcohol | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Nitricacid 50 % | LDPE at 20°C: shows little or damage after 30 days. HDPE at 20°C & LDPE at 50°C: show effect after 7 days. HDPE at 50°C: shows immediate damage and is not recommended. |
| Nitricacid 70 % | LDPE / HDPE at 20°C: show some effect after 7 days. LDPE / HDPE at 50°C: show immediate damage. Not recommended. |
| n-octane | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Oleic acid | HDPE at 20°C-50°C: little or no damage after 30 days. LDPE at 20°C-50°C: shows immediate damage and is not recommended. |
| Oxalic acid | LDPE at 20°C: shows some effect after 7 days. HDPE at 20°C and LDPE / HDPE at 50°C: shows little/ no damage after 30 days. |
| Ozone | LDPE / HDPE at 20°C: little or no damage after 30 days. LDPE / HDPE at 50°C: show immediate damage. Not recommended. |
| Perchloric acid | LDPE / HDPE at 20°C: little or no damage after 30 days. LDPE / HDPE at 50°C: show immediate damage. Not recommended. |
| Perchloric ethylene | LDPE / HDPE at 20°C-50°C: show immediate damage. Not recommended. |
| Phenol | LDPE / HDPE at 20°C-50°C: show immediate damage. Not recommended. |
| Phosphoric acid 10% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Phosphoric acid 85% | LDPE / HDPE at 20°C: little or no damage after 30 days. LDPE at 50°C: shows immediate damage and is not recommended. |
| Phosphorous trichloride | LDPE / HDPE at 20°C: little or no damage after 30 days. LDPE at 50°C: has no data available. HDPE at 50°C: shows some effect after 7 days. |
| Potassium carbonate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Potassium hydroxide 5 % | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Potassium hydroxide concentrated | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Potassium permanganate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Propylene glycol | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Pyridine | Immediate damage may occur. Not recommended for continuous use. |
| Salicylic acid, saturated | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Silver acetate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Silver nitrate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Sodium carbonate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Sodium chloride, saturated | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Sodium dichromate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Sodium hydroxide 1% | LDPE at 20°C-50°C: shows little or no damage after 30 days. HDPE at 20°C-50°C: shows some effect after 7 days. |
| Sodium hydroxide 50% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Sodium hypochlorite 15% | HDPE at 20°C-50°C: little or no damage after 30 days. LDPE at 20°C: is suitable but at 50°C: shows some effect after 7 days. |
| Sodium nitrate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Sodium sulphate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Sucrose | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Sulfuric acid 20% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Sulfuric acid 6% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Sulfuric acid 60% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Sulfuric acid 98% | LDPE at 20°C-50°C: shows little or no damage after 30 days. HDPE at 20°C: shows effect after 7 days. Not recommended for use at 50°C. |
| Tannic acid | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Tetrahydrofuran | LDPE / HDPE at 20°C: show some effect after 7 day of constant exposure. LDPE / HDPE at 50°C: show immediate damage. Not recommended. |
| Toluene | LDPE at 20°C: show some effect after 7 day of constant exposure. HDPE at 20°C-50°C & LDPE at 50°C: show immediate damage. Not recommended. |
| Trichloracetic acid | LDPE / HDPE at 20°C: show some effect after 7 day of constant exposure. LDPE / HDPE at 50°C: show immediate damage. Not recommended. |
| Trichlorethane | Immediate damage may occur. Not recommended for continuous use. |
| Turpentine oil | LDPE / HDPE at 20°C: show some effect after 7 days. LDPE / HDPE at 50°C: show immediate damage. Not recommended. |
| Urea | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
| Xylene | HDPE at 20°C: shows some effect after 7 day of constant exposure. LDPE at 20-50°C and HDPE at 50°C: show immediate damage. Not recommended. |
| Zinc chloride | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |